JILIR CERAMIC CO., LTD







   Production

Capability of Some main grinding media products:

  

Complete-stabilized Zirconia bead
Character:
Real density: 5.9
Bulk density: 3.6
Hardness: 7 mohs
Using range:
Vertical, horizontal high-speed pin mill, good effect for high viscosity material. Linear speed 25 m/s
Features:
10-20 times longer life than fusion-method Zirconia, increase more than 40% of the production efficiency. Without break and blowhole, it is very well-accepted in many foreign enterprises for several years.



Partial- stabilized Zirconia bead
Character:
Real density: 5.9
Bulk density: 3.6
Hardness: 7 mohs
Using range:
Vertical, horizontal high-speed mill, Linear speed 25 m/s, for grinding of high viscosity material
Features:
5-7 times longer life than fusion-method Zirconia, increase more than 30% of the production efficiency. Without break and blowhole.



Compound Zircon bead
Character
Real density: 3.7
Bulk density: 2.1
Hardness: 9 mohs
Using range:
Low or medium-speed mill, Linear speed 13-17 m/s, for grinding of material with medium viscosity or 60-80% solid content
Features:
A little higher consumption than fusion-method Zirconia, but without break, price is 50% lower.



Hard ceramic bead
Character:
Real density: 2.7
Bulk density: 1.7
Hardness: 7 mohs
Using range:
Mill with a linear speed of 11-15 m/s, for grinding of material with medium viscosity or 50-70% solid content
Features:
For water-washed Kaolin milling, solid content can be increased 15% and without top-rising comparing with Kaolin beads. Do not build up screen, high fluidity, without break.